不锈钢成分对照表 |
|||||||||||
| 序号 | 牌号 | 化学成分 |
|||||||||
C 碳 |
Si 硅 |
Mn 锰 |
P 磷 |
S 硫 |
Ni 镍 |
Cr 铬 |
Mo 钼 |
Ti 钛 |
其它 |
||
1 |
0Cr18Ni9 |
≤0.07 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
8.00-11.00 |
17.00-19.00 |
|
- |
- |
2 |
1Cr18Ni9 |
≤0.15 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
8.00-10.00 |
17.00-19.00 |
|
|
|
3 |
1Cr18Ni9Ti |
≤0.12 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
8.00-11.00 |
17.00-19.00 |
|
5(C%-0.02)-0.80 |
|
4 |
00Cr19Ni10 |
≤0.03 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
8.00-12.00 |
18.00-20.00 |
- |
- |
- |
5 |
0Cr23Ni13 |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
12.00-15.00 |
22.00-24.00 |
- |
- |
- |
6 |
0Cr25Ni20 |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
19.00-22.00 |
24.00-26.00 |
- |
5C%-0.07 |
- |
7 |
0Cr18Ni10Ti |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
9.00-12.00 |
17.00-19.00 |
- |
≥5C% |
- |
8 |
0Cr18Ni11Nb |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
9.00-13.00 |
17.00-19.00 |
- |
- |
Nb≥10C% |
9 |
00Cr18Ni10N |
≤0.030 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
8.50-11.50 |
17.00-19.00 |
|
|
N;0.12-0.22 |
10 |
0Cr19Ni9N |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
7.00-10.50 |
18.00-20.00 |
|
|
N;0.10-0.25 |
11 |
0Cr19Ni10NbN |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
7.00-10.50 |
18.00-20.00 |
|
|
Nb≤0.15N;0.15-030 |
12 |
0Cr17Ni12Mo2 |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
10.00-14.00 |
16.00-18.50 |
2.00-3.00 |
- |
- |
13 |
00Cr17Ni14Mo2 |
≤0.03 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
12.00-15.00 |
16.00-18.00 |
2.00-3.00 |
- |
- |
14 |
00Cr17Ni13Mo2N |
≤0.03 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
10.50-14.50 |
16.00-18.50 |
2.00-3.00 |
|
0.12-0.22 |
15 |
0Cr17Ni12Mo2N |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
10.00-14.00 |
16.00-18.00 |
2.00-3.00 |
|
0.10-0.22 |
16 |
0Cr19Ni13Mo3 |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
11.00-15.00 |
18.00-20.00 |
3.00-4.00 |
- |
- |
17 |
00Cr19Ni13Mo3 |
≤0.03 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
11.00-15.00 |
18.00-20.00 |
3.00-4.00 |
- |
- |
18 |
0Cr18Ni12Mo2Ti |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
11.00-14.00 |
16.00-19.00 |
1.80-2.50 |
5C%-0.70 |
- |
19 |
1Cr18Ni12Mo2Ti |
≤0.12 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
11.00-14.00 |
16.00-19.00 |
1.80-2.50 |
5(C%-0.02)-0.80 |
- |
20 |
0Cr18Ni12Mo3Ti |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
11.00-14.00 |
16.00-19.00 |
2.50-3.50 |
5C%-0.70 |
- |
21 |
1Cr18Ni12Mo3Ti |
≤0.12 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
11.00-14.00 |
16.00-19.00 |
2.50-3.50 |
5(C%-0.02)-0.80 |
- |
22 |
0Cr18Ni12Mo2Cu2 |
≤0.08 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
11.00-14.00 |
17.00-19.00 |
1.20-2.75 |
- |
Cu1.00-2.50 |
23 |
00Cr18Ni14Mo2Cu2 |
≤0.03 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
12.00-16.00 |
17.00-19.00 |
1.20-2.75 |
- |
Cu1.00-2.50 |
24 |
0Cr18Ni9Ti |
≤0.07 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
8.00-11.00 |
17.00-19.00 |
- |
5(C%-0.02)-0.08 |
|
25 |
1Cr17Ni7 |
≤0.07 |
≤1.00 |
≤2.00 |
≤0.035 |
≤0.030 |
6.00-8.00 |
16.00-18.00 |
|
|
|